Terblend N NG-04

Terblend® N NG-04 is a 20% glass fiber reinforced ABS/PA blend with high dimensional stability and rigidity.

Key Features

  • Very high dimensional stability
  • Very high rigidity
  • High softening temperature
  • Glass fiber reinforced (20%)

Applications

  • Automotive parts
  • Overhead consoles
  • Housings
  • Grade Version
  • Properties

    คุณสมบัติของ

    ค่าทั่วไปสำหรับผลิตภัณฑ์ที่ไม่ทำสีที่ 23 องศาเซลเซียส วิธีการทดสอบ หน่วย ค่า
    คุณสมบัติการเปลี่ยนรูปและการไหล
    Melt Volume Rate, 240 °C/10 kg ISO 1133 cm³/10 min 15
    คุณสมบัติทางกล
    Tensile Modulus ISO 527 MPa 5400
    Tensile Stress at Break, 23 °C ISO 527 MPa 60
    Tensile Strain at Break, 23 °C ISO 527 % 3.2
    Flexural Modulus, 23 °C ISO 178 MPa 4500
    Flexural Strength, 23 °C ISO 178 MPa 115
    Charpy Notched Impact Strength, 23° C ISO 179/1eA kJ/m² 8
    Charpy Notched Impact Strength, -30 °C ISO 179/1eA kJ/m² 5
    Charpy Unnotched Impact Strength, 23 °C ISO 579 kJ/m² 30
    Charpy Unnotched Impact Strength, -30 °C ISO 579 kJ/m² 25
    Izod Notched Impact Strength, 23 °C ISO 180/A kJ/m² 9
    Izod Notched Impact Strength, -30 °C ISO 180/A kJ/m² 5
    Hardness, Ball Indentation ISO 2039-1 MPa 107
    คุณสมบัติทางความร้อน
    Vicat Softening Temperature VST/B/50 (50N, 50 °C/h) ISO 306 °C 114
    Vicat Softening Temperature, VST/A/50 (10N, 50 °C/h) ISO 306 °C 180
    Coefficient of Linear Thermal Expansion ISO 11359 10-6/°C 40
    Heat Deflection Temperature A; (unannealed; 1.8 MPa) ISO 75 °C 100
    Heat Deflection Temperature B; (unannealed; 0.45 MPa) ISO 75 °C 164
    คุณสมบัติทางอีเลคทริค
    Relative Permittivity (1 MHz) IEC 62631-2-1 - 2.9
    Dissipation Factor (1 MHz) IEC 62631-2-1 10-4 130
    Volume Resistivity IEC 62631-3-1 Ω*m 1013
    Surface Resistivity IEC 62631-3-1 Ω 1014
    Other Properties
    Density ISO 1183 kg/m³ 1200
    Moisture Absorption, Equilibrium 23 °C/50% RH ISO 62 % 0.9
    Glass Fibre content - % 20
    UL94 rating at 1.5 mm thickness IEC 60695-11-10 - HB
    Processing
    Melt Temperature Range ISO 294 °C 240 - 270
    Mold Temperature Range ISO 294 °C 60 - 80
    Drying Temperature - °C 80 - 90
    Drying Time - h 4 - 8
    Molding shrinkage, free, longitudinal - % 0.3

    Typical values for uncolored products
    Please note that all processing data stated are only indicative and may vary depending on the individual processing complexities.
    Please consult our local sales or technical representatives for details.

  • Processing

    กำลังประมวลผล

  • Safety Data Sheet