物性

２３℃での無色製品の標準値	試験方法	単位	数値
流動学的性質
Melt Volume Rate 220 °C/10 kg	ISO 1133	cm³/10 min	20
機械的性質
Charpy Notched Impact Strength, 23° C	ISO 179/1eA	kJ/m²	22
Charpy Notched Impact Strength, -30 °C	ISO 179/1eA	kJ/m²	11
Charpy Unnotched, 23 °C	ISO 179/1eU	kJ/m²	180
Charpy Unnotched, -30 °C	ISO 179/1eU	kJ/m²	120
Izod Notched Impact Strength, 23 °C	ISO 180/A	kJ/m²	22
Izod Notched Impact Strength, -30 °C	ISO 180/A	kJ/m²	11
Tensile Modulus	ISO 527	MPa	2300
Tensile Stress at Yield, 23 °C	ISO 527	MPa	39
Tensile Strain at Yield, 23 °C	ISO 527	%	2.1
Tensile Stress at Break, 23 °C	ISO 527	MPa	30
Tensile Strain at Break, 23 °C	ISO 527	%	> 15
Nominal Strain at Break, 23 °C	ISO 527	%	15
Flexural Modulus, 23 °C	ISO 178	MPa	2100
Flexural Strength, 23 °C	ISO 178	MPa	60
Hardness, Ball Indentation	ISO 2039-1	MPa	97
熱的性質
Vicat Softening Temperature, VST/B/120 (50N, 120 °C/h)	ISO 306	°C	100
Vicat Softening Temperature VST/B/50 (50N, 50 °C/h)	ISO 306	°C	98
Heat Deflection Temperature A; (annealed 4 h/80 °C; 1.8 MPa)	ISO 75	°C	93
Heat Deflection Temperature B; (annealed 4 h/80 °C; 0.45 MPa)	ISO 75	°C	97
Coefficient of Linear Thermal Expansion	ISO 11359	10-6/°C	100
電気的性質
Dielectric Strength, Short Time, 1.0 mm	IEC 60243-1	kV/mm	33
Comparative Tracking Index	IEC 60112	V	600
進行中
Density	ISO 1183	kg/m³	1040
UL94 rating at 1.5 mm thickness	IEC 60695-11-10	-	HB
Processing
Linear Mold Shrinkage	ISO 294-4	%	0.4 - 0.7
Melt Temperature Range	ISO 294	°C	230 - 260
Mold Temperature Range	ISO 294	°C	60 - 80
Drying Temperature	-	°C	80
Drying Time	-	h	2 - 4

Typical values for uncolored products
Please note that all processing data stated are only indicative and may vary depending on the individual processing complexities.
Please consult our local sales or technical representatives for details.

進行中

Choose grade version

製品安全データシートのダウンロード