LURAN HH-120
Luran® HH-120 is a grade of AMSAN with high heat resistance and improved mechanical strength. It is suitable for injection molding and extrusion applications and can be used as a modifier for high heat ABS and PVC.
Key Features
- Dimensional stability
- Heat resistance
- High surface quality
Applications
- Automotive exterior trim : mirror housings, exterior pillars & trims, spoilers
-
Grade Version
-
Properties
属性
无色产品在摄氏 23 度时的典型值 测试方法 单位 数值 流变性能 Melt Volume Rate 220 °C/10 kg ISO 1133 cm³/10 min 7 机械性能 Charpy Notched Impact Strength, 23° C ISO 179/1eA kJ/m² 2 Charpy Unnotched, 23 °C ISO 179/1eU kJ/m² 20 Charpy Unnotched, -30 °C ISO 179/1eU kJ/m² 21 Izod Notched Impact Strength, 23 °C ISO 180/A kJ/m² 2 Tensile Modulus ISO 527 MPa 3900 Tensile Stress at Yield, 23 °C ISO 527 MPa 79 Tensile Strain at Break, 23 °C ISO 527 % 3 Flexural Modulus, 23 °C ISO 178 MPa 3900 Flexural Strength, 23 °C ISO 178 MPa 135 Hardness, Ball Indentation ISO 2039-1 MPa 175 热性能 Vicat Softening Temperature VST/B/50 (50N, 50 °C/h) ISO 306 °C 120 Heat Deflection Temperature A; (annealed 4 h/80 °C; 1.8 MPa) ISO 75 °C 104 Heat Deflection Temperature B; (annealed 4 h/80 °C; 0.45 MPa) ISO 75 °C 110 Coefficient of Linear Thermal Expansion ISO 11359 10-6/°C 70 Thermal Conductivity ISO 22007-4 W/(m K) 0.17 其他属性 Refractive Index, Sodium D Line ISO 489 - 1.567 Haze ASTM D 1003 % < 1 Light Transmission at 550 nm ASTM D 1003 % > 89 Other Properties Density ISO 1183 kg/m³ 1080 Moisture Absorption, Equilibrium 23 °C/50% RH ISO 62 % 0.3 Processing Melt Temperature Range ISO 294 °C 220 - 270 Mold Temperature Range ISO 294 °C 40 - 80 Drying Temperature - °C 80 Drying Time - h 2 - 4 Linear Mold Shrinkage ISO 294-4 % 0.3 - 0.7 Typical values for uncolored products
Please note that all processing data stated are only indicative and may vary depending on the individual processing complexities.
Please consult our local sales or technical representatives for details. -